Products
Hongrui Plastic
PA66
| Item | Test Standard | Unit | Typical Performance | ||||||||||||||||
| A1000 | A1304 | A1305 | A201 | A401 | A303 | A304 | A305 | A306 | A309 | A3010 | A500 | A830 | A860 | A326 | A333 | A353 | |||
| Density | D792 | g/cm3 | 1.24 | 1.40 | 1.45 | 1.08 | 1.09 | 1.23 | 1.28 | 1.32 | 1.36 | 1.52 | 1.56 | 1.14 | 1.24 | 1.35 | 1.36 | 1.35 | 1.42 |
| Tensile Strength | D638 | MPa | 60 | 80 | 100 | 45 | 60 | 115 | 125 | 145 | 180 | 190 | 195 | 80 | 70 | 70 | 145 | 110 | 120 |
| Elongation at Break | D638 | % | 3 | 2 | 2 | 100 | 10 | 2 | 2 | 2 | 2 | 2 | 2 | 3 | 3 | 2 | 3 | 2 | 2 |
| Bending Strength | D790 | MPa | 80 | 160 | 180 | 55 | 70 | 145 | 170 | 200 | 240 | 260 | 280 | 100 | 90 | 100 | 200 | 160 | 200 |
| Flexural Modulus | D790 | MPa | 2400 | 5000 | 7000 | 1600 | 2000 | 4500 | 5000 | 6000 | 8000 | 9000 | 10000 | 2700 | 2800 | 3500 | 6500 | 5000 | 8000 |
| Notched Impact Strength of Cantilever | D256 | kJ/㎡ | 6.0 | 6.0 | 7.0 | 80.0 | 12.0 | 7.0 | 7.0 | 8.0 | 9.0 | 8.0 | 10.0 | 4.5 | 6.0 | 6.0 | 18.0 | 6.0 | 5.0 |
| Rockwell Hardness, HRR | D785 | —— | 115 | 120 | 120 | 110 | 113 | 120 | 120 | 120 | 120 | 120 | 120 | 115 | 118 | 120 | 120 | 120 | 120 |
| Melting Point | ℃ | 255 | 255 | 260 | 258 | 260 | 260 | 262 | 263 | 263 | 263 | 263 | 260 | 260 | 260 | 260 | 260 | 262 | |
| Heat Distortion Temperature, 0.45MPa | D648 | ℃ | 190 | 210 | 240 | 180 | 200 | 235 | 240 | 245 | 250 | 255 | 255 | 210 | 190 | 200 | 245 | 235 | 250 |
| Flame Retardance | UL94 | 級(jí) | V0 | V0 | V0 | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB |
| Surface Resistance | D257 | Ω | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 |
| Dielectric Strength | D149 | KV/mm | 17 | 17 | 17 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 |
| Mould Shrinkage | D955 | mm/mm | 0.012 | 0.003 | 0.001 | 0.018 | 0.015 | 0.004 | 0.003 | 0.002 | 0.001 | 0.001 | 0.001 | 0.013 | 0.008 | 0.006 | 0.003 | 0.003 | 0.001 |
| Filling Amount | % | —— | GF20 | GF25 | —— | —— | GF15 | GF20 | GF25 | GF30 | GF45 | GF50 | —— | M15 | M30 | GF30 |
GF15+ M15 |
GF15+ M25 |
|
| Features | General flame retardant type | Glass fiber reinforced flame retardant type | Toughening high impact type | Glass fiber reinforced type | General type | Mineral reinforced type | Glass fiber reinforced and toughening type | Glass fiber mineral compound reinforced type | |||||||||||
| Use | Electronics, breaker | Electronics connector | Textile equipment, rail component, sports equipment, pipe, ribbon | Bearing retainer, mechanical parts, auto parts, electronic components | Mechanical parts, connector | Auto wheel casing, mechanical shell | Mechanical parts, auto parts | ||||||||||||
Nanjing Hongrui Plastic Products Co., Ltd.
Add: No.15 Chunyang Road, Bingjiang Development Zone, Jiangning, Nanjing City, Jiangsu Province, China
Postal Code: 211178
Tel: +86-25-66606111
Fax: +86-25-66622608
24-hour duty phone number: +86-13382036816, +86-13382076041
Technical Services: +86-15850506640
E-mail: sales@njhongrui.com , hanbinghr@163.com
Scan
Mobile version
Copyright(C)2025, Nanjing Hongrui Plastic Products Co., Ltd. All Rights Reserved. Supported by Sunsirs ChemNet Toocle Copyright Notice 備案序號(hào)：蘇ICP備12049752號(hào)