Hongrui Plastic
PA6
| Item | Test Standard | Unit | Typical Performance | ||||||||||||||||
| B1000 | B1302 | B1304 | B201 | B401 | B303 | B304 | B305 | B306 | B307 | B3010 | B500 | B820 | B850 | B860 | B326 | B353 | |||
| Density | D792 | g/cm3 | 1.22 | 1.28 | 1.35 | 1.07 | 1.09 | 1.23 | 1.28 | 1.32 | 1.36 | 1.40 | 1.56 | 1.13 | 1.20 | 1.28 | 1.35 | 1.35 | 1.42 |
| Tensile Strength | D638 | MPa | 50 | 70 | 90 | 45 | 60 | 110 | 120 | 145 | 170 | 175 | 190 | 70 | 50 | 55 | 65 | 140 | 120 |
| Elongation at Break | D638 | % | 3 | 2 | 2 | 100 | 10 | 2 | 2 | 2 | 2 | 2 | 2 | 3 | 3 | 3 | 2 | 2 | 2 |
| Bending Strength | D790 | MPa | 60 | 120 | 145 | 55 | 70 | 140 | 165 | 190 | 220 | 230 | 280 | 90 | 60 | 70 | 90 | 180 | 190 |
| Flexural Modulus | D790 | MPa | 2000 | 4000 | 5000 | 1600 | 2000 | 4000 | 4800 | 6000 | 7500 | 8000 | 10000 | 2600 | 2200 | 2500 | 3500 | 6000 | 7500 |
| Notched Impact Strength of Cantilever | D256 | kJ/㎡ | 8.0 | 6.0 | 7.0 | 80.0 | 12.0 | 7.0 | 7.0 | 8.0 | 10.0 | 10.0 | 10.0 | 5.0 | 6.0 | 6.0 | 7.0 | 18.0 | 5.0 |
| Rockwell Hardness, HRR | D785 | —— | 115 | 120 | 120 | 110 | 112 | 120 | 120 | 120 | 120 | 120 | 120 | 115 | 115 | 118 | 120 | 120 | 120 |
| Melting Point | ℃ | 220 | 225 | 225 | 220 | 220 | 225 | 225 | 225 | 225 | 225 | 225 | 225 | 223 | 225 | 225 | 225 | 225 | |
| Heat Distortion Temperature, 0.45MPa | D648 | ℃ | 160 | 190 | 210 | 150 | 160 | 210 | 215 | 220 | 225 | 225 | 235 | 180 | 170 | 200 | 215 | 225 | 230 |
| Flame Retardance | UL94 | 級 | V0 | V0 | V0 | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB | HB |
| Surface Resistance | D257 | Ω | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 | 1013 |
| Dielectric Strength | D149 | KV/mm | 17 | 17 | 17 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 | 20 |
| Mould Shrinkage | D955 | mm/mm | 0.012 | 0.005 | 0.003 | 0.018 | 0.015 | 0.004 | 0.003 | 0.002 | 0.001 | 0.001 | 0.001 | 0.015 | 0.012 | 0.008 | 0.006 | 0.003 | 0.001 |
| Filling Amount | % | —— | GF10 | GF20 | —— | —— | GF15 | GF20 | GF25 | GF30 | GF35 | GF50 | —— | M10 | M25 | GF30 | GF30 |
GF15+ M25 |
|
| Features | General flame retardant type | Glass fiber reinforced flame retardant type | Toughening high impact type | Glass fiber reinforced type | General type | Mineral reinforced type | Glass fiber reinforced and toughening type | Glass fiber mineral compound reinforced type | |||||||||||
| Use | Electronic component | Electronics connector | Textile equipment, rail component, sports equipment, pipe, ribbon | Bearing retainer, mechanical parts, auto parts, electronic components | Mechanical parts, connector | Auto wheel casing, mechanical shell | Mechanical parts, auto parts | ||||||||||||
Nanjing Hongrui Plastic Products Co., Ltd.
Add: No.15 Chunyang Road, Bingjiang Development Zone, Jiangning, Nanjing City, Jiangsu Province, China
Postal Code: 211178
Tel: +86-25-66606111
Fax: +86-25-66622608
24-hour duty phone number: +86-13382036816, +86-13382076041
Technical Services: +86-15850506640
E-mail: sales@njhongrui.com , hanbinghr@163.com
Scan
Mobile version
Copyright(C)2025, Nanjing Hongrui Plastic Products Co., Ltd. All Rights Reserved. Supported by Sunsirs ChemNet Toocle Copyright Notice 備案序號：蘇ICP備12049752號